Production of Sorbitol via Hydrogenation of Glucose over Ruthenium Coordinated with Amino Styrene-co-maleic Anhydride Polymer Encapsulated on Activated Carbon (Ru/ASMA@AC) Catalyst

Abstract

Sorbitol, a product primarily derived from glucose hydrogenation, has extensive applications in the pharmaceutical, chemical and other industries. Amino styrene-co-maleic anhydride polymer encapsulated on activated carbon (Ru/ASMA@AC) catalysts were developed for efficient glucose hydrogenation and were prepared and confined Ru by coordination with styrene-co-maleic anhydride polymer (ASMA). Through single-factor experiments, optimal conditions were determined to be 2.5 wt.% ruthenium loading and a catalyst usage of 1.5 g, 20% glucose solution at 130 °C, reaction pressure of 4.0 MPa, and a stirring speed of 600 rpm for 3 h. These conditions achieved a high glucose conversion rate of 99.68% and a sorbitol selectivity of 93.04%. Reaction kinetics testing proved that the hydrogenation of glucose catalyzed by Ru/ASMA@AC was a first-order reaction, with a reaction activation energy of 73.04 kJ/mol. Furthermore, the catalytic performance of the Ru/ASMA@AC and Ru/AC catalysts for glucose hydrogenation were compared and characterized by various detection methods. The Ru/ASMA@AC catalyst exhibited excellent stability after five cycles, whereas the traditional Ru/AC catalyst suffered from a 10% decrease in sorbitol yield after three cycles. These results suggest that the Ru/ASMA@AC catalyst is a more promising candidate for high-concentration glucose hydrogenation due to its high catalytic performance and superior stability.

Keywords

• Ru/ASMA@AC catalyst
• coordination
• glucose conversion
• sorbitol yield
• confine