Impact of (nano ZnO/multi-wall CNTs) prepared by arc discharge method on the removal efficiency of stable iodine 127I and radioactive iodine 131I from water

Abstract

Abstract Radioactive iodine isotopes especially 131I are used for diagnosis and treatment of different types of cancer diseases. Due to the leak of radioactive iodine into the patient’s urine in turn, the wastewater would be contaminated, so it is worth preparing a novel adsorption green material to remove the radioactive iodine from wastewater efficiently. The removal of 127I and 131I contaminants from aqueous solution is a problem of interest. Therefore, this work presents a new study for removing the stable iodine 127I− and radioactive iodine 131I from aqueous solutions by using the novel nano adsorbent (Nano ZnO/MWCNTs) which is synthesized by the arc discharge method. It is an economic method for treating contaminated water from undesired dissolved iodine isotopes. The optimal conditions for maximum removal are (5 mg/100 ml) as optimum dose with shacking (200 rpm) for contact time of (60 min), at (25 °C) in an acidic medium of (pH = 5). After the adsorption process, the solution is filtrated and the residual iodide (127I−) is measured at a maximum UV wavelength absorbance of 225 nm. The maximum adsorption capacity is (15.25 mg/g); therefore the prepared nano adsorbent (Nano ZnO/MWCNTs) is suitable for treating polluted water from low iodide concentrations. The adsorption mechanism of 127I− on to the surface of (Nano ZnO/MWCNTs) is multilayer physical adsorption according to Freundlich isotherm model and obeys the Pseudo-first order kinetic model. According to Temkin isotherm model the adsorption is exothermic. The removal efficiency of Nano ZnO/MWCNTs for stable iodine (127I−) from aqueous solutions has reached 97.23%, 89.75%, and 64.78% in case of initial concentrations; 0.1843 ppm, 0.5014 ppm and 1.0331 ppm, respectively. For the prepared radio iodine (131I−) solution of radioactivity (20 µCi), the dose of nano adsorbent was (10 mg/100 ml) and the contact time was (60 min) at (pH = 5) with shacking (200 rpm) at (25 °C). The filtration process was done by using a syringe filter of a pore size (450 nm) after 2 days to equilibrate. The removal efficiency reached (34.16%) after the first cycle of treatment and the percentage of residual radio iodine was (65.86%). The removal efficiency reached (94.76%) after five cycles of treatment and the percentage of residual radio iodine was (5.24%). This last percentage was less than (42.15%) which produces due to the natural decay during 10 days.

Keywords

• Nano ZnO/MWCNTs
• Nano adsorbents
• Iodine 127
• Iodine 131
• Water treatments
• Kinetic models