Weathering Stability and Durability of Birch Plywood Modified with Different Molecular Weight Phenol-Formaldehyde Oligomers

Abstract

This study investigated the effect of phenol-formaldehyde (PF) resin treatment on the weathering stability and biological durability of birch plywood. Silver birch (Betula pendula) veneers were vacuum-pressure impregnated with four different PF resins with average molecular weights (Mw) of 292 (resin A), 528 (resin B), 703 (resin C), and 884 g/mol (resin D). The aging properties of PF resin modified birch plywood were analyzed using artificial weathering with ultraviolet (UV) light, UV and water spray, and weathering under outdoor conditions. The same combinations of PF-treated plywood specimens were then tested in soil-bed tests to determine their resistance against soft-rot wood decay. It was not possible to compare weathering processes under artificial conditions to processes under outdoor conditions. However, the weathering stability of birch plywood treated with PF resins A, B, and C, scored better than plywood treated with commercial resin D (regardless of solid content concentration [%]). Results from unsterile soil bed tests showed improvements in resistance to soft-rot wood decay compared to untreated plywood and solid wood. Mass loss [%] was lowest for birch plywood specimens treated with resin of highest solid content concentration (resin D, 20%). Provisional durability ratings delivered durability class (DC) ratings of 2–3, considerably improved over untreated solid wood and untreated birch plywood (DC 5).

Keywords

• birch plywood
• molecular weight
• phenol-formaldehyde resin
• soft-rot
• weathering stability