Effect of Mn/Ag Ratio on Microstructure and Mechanical Properties of Heat-Resistant Al-Cu Alloys

Abstract

This paper mainly investigated the effect of the Mn/Ag ratio on the microstructure and room temperature and high-temperature (350 °C) tensile mechanical properties of the as-cast and heat-treated Al-6Cu-xMn-yAg (x + y = 0.8, wt.%) alloys. The as-cast alloy has α-Al, Al2Cu, and a small amount of Al7Cu2 (Fe, Mn) and Al20Cu2 (Mn, Fe)3 phases. After T6 heat treatment, a massive dispersive and fine θ′-Al2Cu phase (100~400 nm) is precipitated from the matrix. The Mn/Ag ratio influences the quantity and size of the precipitates; when the Mn/Ag ratio is 1:1, the θ′-Al2Cu precipitation quantity reaches the highest and smallest. Compared with the as-cast alloy, the tensile strength of the heat-treated alloy at room temperature and high temperature is greatly improved. The strengthening effect of the alloy is mainly attributed to the nanoparticles precipitated from the matrix. The Mn/Ag ratio also affects the high-temperature tensile mechanical properties of the alloy. The high-temperature tensile strength of the alloy with a 1:1 Mn/Ag ratio is the highest, reaching 135.89 MPa, 42.95% higher than that of the as-cast alloy. The analysis shows that a synergistic effect between Mn and Ag elements can promote the precipitation and refinement of the θ′-Al2Cu phase, and there is an optimal ratio (1:1) that obtains the lowest interfacial energy for co-segregation of Mn and Ag at the θ′/Al interface that makes θ′-Al2Cu have the best resistance to coarsening.

Keywords

• Al-Cu-Mn-Ag alloy
• Mn/Ag ratio
• microstructure
• high-temperature tensile mechanical property