Investigation of the Stability of the Poly(ethylene oxide)|LiNi1‐x‐y CoxMnyO2 Interface in Solid‐State Batteries

Abstract

Abstract While solid‐state batteries (SSBs) comprising poly(ethylene oxide) (PEO) based electrolytes are successfully commercialized already for operation at elevated temperature, the selection of the cathode active material (CAM) has so far been limited to LiFePO4. When using high‐voltage CAMs such as LiNi1‐x‐yCoxMnyO2 (NCM), the cells experience fast capacity fading – the cause of which is not consistently understood in literature. In this study, electrochemical impedance spectroscopy measurements in a three‐electrode setup are applied to confirm that the NCM|PEO interface is indeed the Achilles' heel in PEO‐based SSBs at high voltages. In this regard, the interfacial stability on the cathode side depends not only on the upper cut‐off voltage, but also on the molecular weight of PEO, strongly affecting the cell performance. Scanning electron microscopy images of the cathodes after cycling suggest that at high voltages interfacial degradation leads to fragmentation of the polymer backbone and to a decrease in viscosity of the solid polymer electrolyte. Overall, the results help to understand the detrimental processes occurring in PEO‐based SSBs in combination with high‐voltage cathodes.

Keywords

• high‐voltage cathode active materials
• interface stability
• poly(ethylene oxide) (PEO)
• solid polymer electrolytes
• solid‐state batteries