Electron-Beam Welding of Titanium and Ti6Al4V Using Magnetron-Sputtered Nb, V, and Cu Fillers

Abstract

In this work, the results of an investigation of electron-beam-welded samples of commercially pure titanium (CP-Ti) and the titanium alloy Ti6Al4V (Ti64) using fillers of various beta-stabilizing elements (Nb, V, Cu) are presented. The fillers were in the form of deposited layers on each of the two specimens via DC magnetron sputtering. The specimens were then subjected to electron-beam welding (EBW) under the same technological conditions. The structure of the obtained welded joints was investigated by scanning electron microscopy (SEM). X-ray diffraction (XRD) was used to investigate the phase composition of the fusion zone (FZ). The study of the mechanical properties of the samples was carried out via tensile tests and microhardness measurements. The results showed a different influence of the used fillers on the structure and properties of the obtained joints, and in all cases, the yield strength increased compared to the samples welded using the same technological conditions without the use of filler material. In the case of using Nb and V as a filler, the typical transformation of titanium welds into elongated αTi particles along with α’-Ti martensitic structures was observed. The addition of a Cu filler into the structure of the welds resulted in a unification and refining of the structure of the last, which resulted in the improvement of the mechanical properties of the weld, particularly its ductility, which is a known issue where electron-beam welding is concerned.

Keywords

• electron-beam welding
• CP-Ti
• Ti6V4Al
• magnetron sputtering
• fillers
• structure