Extraction of Lead and Zinc from a Rotary Kiln Oxidizing Roasting Cinder

Abstract

In this study, sulfuric acid leaching and gravity shaking-table separation by shaking a table are used to extract lead and zinc from a Pb-Zn oxidizing roasting cinder. The oxidizing roasting cinder—containing 16.9% Pb, 30.5% Zn, 10.3% Fe and 25.1% S—was obtained from a Pb-Zn sulfide ore in the Hanyuan area of China by a flotation-rotary kiln oxidizing roasting process. Anglesite and lead oxide were the main Pb-bearing minerals, while zinc sulfate, zinc oxide and zinc ferrite were the main Zn-bearing minerals. The results show that a part of lead contained in lead oxide is transformed to anglesite, and a 3PbO·PbSO4·H2O-dominated new lead mineral phase after acid leaching. A zinc leaching efficiency of 96.7% was obtained under the leaching conditions used: a leaching temperature of 55 °C; a leaching time of 90 min; a sulfuric acid dosage of 20%; a sulfurous acid dosage of 4%; a cinder particle size of R = 1:4. After the gravity shaking-table separation, a lead concentrate with 50.2% Pb, 2.33% Zn and lead recovery of 86.0% was produced. The main chemical compounds in leaching residue are anglesite, 3PbO·PbSO4·H2O, SiO2 and ZnFe2O4, while the main chemical compounds in lead concentrate are anglesite, 3PbO·PbSO4·H2O and SiO2.

Keywords

• lead
• zinc
• oxidizing roasting cinder
• acid leaching
• gravity separation