High Energy Density in All-Organic Polyimide-Based Composite Film by Doping of Polyvinylidene Fluoride-Based Relaxor Ferroelectrics

Abstract

Recently, due to the advantages of superior compatibility, fewer interface defects, and a high electric breakdown field, all-organic dielectric composites have attracted significant research interest. In this investigation, we produced all-organic P(VDF-TrFE-CFE) terpolymer/PI (terp/PI) composite films by incorporating a small amount of terpolymer into PI substrates for high energy density capacitor applications. The resulting terp/PI-5 (5% terpolymer) composite films exhibit a permittivity of 3.81 at 1 kHz, which is 18.7% greater than that of pristine PI (3.21). Furthermore, the terp/PI-5 film exhibited the highest energy density (9.67 J/cm3) and a relatively high charge–discharge efficiency (84.7%) among the terp/PI composite films. The energy density of the terp/PI-5 film was increased by 59.8% compared to that of the pristine PI film. The TSDC results and band structure analysis revealed the presence of deeper traps in the terp/PI composites, contributing to the suppression of leakage current and improved charge–discharge efficiency. Furthermore, durability tests confirm the stability of the composite films under extended high-temperature exposure and cycling, establishing their viability for practical applications.

Keywords

• all-organic composites
• high energy density
• PVDF-based relaxor ferroelectrics
• high-temperature capacitors
• polyimide film