International Journal of Nanomedicine (May 2024)

On the Ion Implantation Synthesis of Ag-Embedded Over Sr-Substituted Hydroxyapatite on a Nano-Topography Patterned Ti for Application in Acetabular Fracture Sites

  • Swain S,
  • Pradhan M,
  • Bhuyan S,
  • Misra RDK,
  • Rautray TR

Journal volume & issue
Vol. Volume 19
pp. 4515 – 4531

Abstract

Read online

Subhasmita Swain,1 Monalisa Pradhan,1,* Samapika Bhuyan,1,* RDK Misra,2 Tapash R Rautray1 1Biomaterials and Tissue Regeneration Laboratory, Centre of Excellence, Siksha ‘O’ Anusandhan (Deemed to Be University), Bhubaneswar, Odisha, 751030, India; 2Metallurgical, Materials and Biomedical Engineering Department, the University of Texas at El Paso, El Paso, TX, 79968, USA*These authors contributed equally to this workCorrespondence: Tapash R Rautray, Tel +91 9040000604, Email [email protected]: There is an ongoing need for improved healing response and expedited osseointegration on the Ti implants in acetabular fracture sites. To achieve adequate bonding and mechanical stability between the implant surface and the acetabular fracture, a new coating technology must be developed to promote bone integration and prevent bacterial growth.Methods: A cylindrical Ti substrate mounted on a rotating specimen holder was used to implant Ca2+, P2+, and Sr2+ ions at energies of 100 KeV, 75 KeV and 180 KeV, respectively, using a low-energy accelerator to synthesize strontium-substituted hydroxyapatite at varying conditions. Ag2+ ions of energy 100 KeV were subsequently implanted on the as-formed surface at the near-surface region to provide anti-bacterial properties to the as-formed specimen.Results: The properties of the as-formed ion-implanted specimen were compared with the SrHA-Ag synthesized specimens by cathodic deposition and low-temperature high-speed collision technique. The adhesion strength of the ion-implanted specimen was 43 ± 2.3 MPa, which is well above the ASTM standard for Ca-P coating on Ti. Live/dead cell analysis showed higher osteoblast activity on the ion-implanted specimen than the other two. Ag in the SrHA implanted Ti by ion implantation process showed superior antibacterial activity.Discussion: In the ion implantation technique, nano-topography patterned surfaces are not concealed after implantation, and their efficacy in interacting with the osteoblasts is retained. Although all three studies examined the antibacterial effects of Ag2+ ions and the ability to promote bone tissue formation by MC3T3-E1 cells on SrHA-Ag/Ti surfaces, ion implantation techniques demonstrated superior ability. The synthesized specimen can be used as an effective implant in acetabular fracture sites based on their mechanical and biological properties.Keywords: titanium, SrHA-Ag, ion implantation, osteogenic, anti-bacterial

Keywords