Impacts of Nano SiO₂ Addition on the Formation of Ultrafine Particulate Matter during Coal Combustion

Abstract

Clay minerals composed of Si and Al could help reduce ultrafine particulate matter (PM) formation as an additive during coal combustion while currently unacceptable high adding dosages (normally 3–5 wt.%) are required due to their inadequate capture efficiency. To find additives that could effectively reduce the formation of ultrafine PM, coal combustion with a novel nano SiO2 additive (10 was sampled to characterize their particle size distribution, mass yield, size-resolved composition and micromorphology. The results showed that adding a small dosage (0.6%) of nano SiO2 reduced the mass yield of ultrafine PM by 30.70%, showing a much higher ultrafine PM capture efficiency than an existing micron-sized natural clay mineral. However, its performance on different coals varied due to disparities in ash content and composition in coal. A composition analysis revealed that the Na content in the ultrafine PM was decreased after adding nano SiO2, indicating that nano SiO2 inhibited the migration of volatile alkali metals such as Na into ultrafine PM because the Na-containing mineral vapor reacted with the nano SiO2 additive particles with a large specific surface area at a high temperature and inhibited their transformation into ultrafine PM via homogenous nucleation. Changes in the element size distributions and micromorphology showed that the majority of the added nano SiO2 particles reacted or coalesced with each other and/or the minerals embedded in coal, finally growing into a larger PM.

Keywords

• nano additive
• ultrafine particulate matter
• coal combustion
• SiO₂
• alkali metal