Corrosion Behavior of Different Brass Alloys for Drinking Water Distribution Systems

Abstract

Some α + β’ brass components of drinking water distribution systems in Morocco underwent early failures and were investigated to assess the nature and extent of the corrosion attacks. They exhibited different corrosion forms, often accompanied by extensive β’ dezincification. In order to offer viable alternatives to these traditional low cost materials, the corrosion behavior of two representative α + β’ brass components was compared to that of brass alloys with nominal compositions CuZn36Pb2As and CuZn21Si3P, marketed as dezincification resistant. CuZn21Si3P is a recently developed eco-friendly brass produced without any arsenic or lead. Electrochemical tests in simulated drinking water showed that after 10 days of immersion CuZn21Si3P exhibited the highest polarization resistance (Rp) values but after longer immersion periods its Rp values became comparable or lower than those of the other alloys. After 150 days, scanning electron microscope coupled to energy dispersive spectroscopy (SEM-EDS) analyses evidenced that the highest dezincification resistance was afforded by CuZn36Pb2As (longitudinal section of extruded bar), exhibiting dealloying and subsequent oxidation of β’ only at a small depth. Limited surface dealloying was also found on CuZn21Si3P, which underwent selective silicon and zinc dissolution and negligible inner oxidation of both α and κ constituent phases, likely due to peculiar galvanic effects.

Keywords

• brass
• CuZn36Pb2As
• CuZn21Si3P
• corrosion
• dezincification
• simulated drinking water
• EIS
• SEM-EDS
• long immersion