Evaluation of New, Sputtered Carbon SPME Fibers with a Multi-Functional Group Test Mixture

  • Dhananjay I. Patel,
  • Tuhin Roychowdhury,
  • Collin Jacobsen,
  • Colton Myers,
  • Jason S. Herrington,
  • Matthew R. Linford

DOI
https://doi.org/10.3390/separations8120228
Journal volume & issue
Vol. 8, no. 12
p. 228

Abstract

Read online

We report the first fabrication of sputtered carbon, solid-phase microextraction (SPME) fibers. These fibers have competitive extraction capabilities compared with the commercial carbon wide range (CWR) SPME fiber. This report also includes a demonstration of a newly developed SPME test mix that includes 15 different compounds with a wide range of functional groups and chemical properties. The fiber fabrication process involves sputtering carbon onto fused silica fibers, and the effects of throw distance on the morphology of the carbon coatings were studied. Four different carbon coating thicknesses were evaluated, with PDMS added as a stationary phase. These fibers were characterized with multiple analytical techniques, including scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), water contact angle (WCA) goniometry, as well as headspace (HS) and direct immersion (DI)–SPME–GC–MS. The best (11.5 µm) sputtered carbon SPME fibers, with and without PDMS, were evaluated using the new evaluation mix and compared with the commercial CWR fiber and a previously sputtered/developed silicon fiber. The new probe mix helped elucidate differences among the fibers, which would have been missed by current commercial test mixes. The sputtered carbon SPME fibers showed similar functional group selectivity as commercial CWR fibers. However, the sputtered carbon fibers showed higher responses per volume compared with the commercial CWR fiber, indicating the porous morphology of the sputtered carbon has the ability to overcome large phase thickness/volume discrepancies and increase the relative recovery for various compounds.

Keywords