A DOPO-Based Compound Containing Aminophenyl Silicone Oil for Reducing Fire Hazards of Polycarbonate
Xiaoqing Song,
Wendi Xu,
Boyu Cai,
Luze Wang,
Zhonglin Luo,
Biaobing Wang
Affiliations
Xiaoqing Song
Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, School of Materials Science and Engineering, Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering, Changzhou University, Changzhou 213164, China
Wendi Xu
Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, School of Materials Science and Engineering, Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering, Changzhou University, Changzhou 213164, China
Boyu Cai
Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, School of Materials Science and Engineering, Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering, Changzhou University, Changzhou 213164, China
Luze Wang
Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, School of Materials Science and Engineering, Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering, Changzhou University, Changzhou 213164, China
Zhonglin Luo
Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, School of Materials Science and Engineering, Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering, Changzhou University, Changzhou 213164, China
Biaobing Wang
Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, School of Materials Science and Engineering, Jiangsu Collaborative Innovation Center of Photovoltaic Science and Engineering, Changzhou University, Changzhou 213164, China
A novel P/N/Si-containing flame retardant (marked as DASO) was synthesized through an Atherton–Todd reaction between 9,10-dihydro-9-oxa-10-phospha-phenanthrene-10-oxide and aminophenyl silicone oil, and further used for reducing fire hazards of polycarbonate (PC). The chemical structure of DASO was verified via FTIR, 1H, and 31P NMR. Upon the incorporation of 2 wt% DASO, the FRPC composite achieved a high limiting oxygen index (LOI) of 32.2% and a desired UL-94 V-0 rating. In this case, the peak heat release rate (PHRR) and total smoke production (TSP) were reduced by 26% and 44% as compared with the pure PC, respectively. The improved fire safety contributed to the flame retardant roles of DASO in both the condensed phase and gas phase. The presence of DASO promoted the formation of dense and highly graphited char layer in the condensed phase, and released non-combustible gases and phosphorus-containing radicals in the gas phase. Furthermore, the FRPC composites displayed comparable elongation at break but a slightly reduced tensile and impact strength.