Boletín de la Sociedad Española de Cerámica y Vidrio (Oct 1999)
Resultados preliminares sobre un proceso Sol-Gel para la síntesis de disoluciones precursoras de láminas delgadas ferroeléctricas con estructura de Perovskita laminar
Abstract
SrBi2Ta2O9 precursor solutions have been prepared by sol-gel using, as reactives, tantalum ethoxide and strontium and bismuth 2-ethyl-hexanoates. These compounds were disolved in 1,3-propanediol as majoritary solvent. The resulting solutions had low hydrolysis and condensation, thus making possible their manipulation and storage in atmospheres with moisture. Films deposited from these solutions were crystallised at 750ºC, developing, as majoritary phase, the SrBi2Ta2O9 layered perovskite. Electric poling of these films indicates a moderate ferroelectric response with values of remanent polarisation of Pr~1μC/cm2.<br><br>Se han preparado por sol-gel soluciones precursoras de SrBi2Ta2O9, utilizando como reactivos el etóxido de tántalo y los 2-etilhexanoatos de estroncio y de bismuto. Como disolvente mayoritario se empleó el 1,3-propanodiol. Las soluciones resultantes presentaron una baja velocidad de hidrólisis y condensación, haciendo posible su almacenaje y manipulación en atmósferas no exentas de humedad. Las láminas derivadas de estas soluciones y cristalizadas a 750ºC presentaron como fase mayoritaria la perovskita laminar de SrBi2Ta2O9. La polarización eléctrica de estas láminas puso de manifiesto una moderada actividad ferroeléctrica, con valores de polarización remanente de Pr~1μC/cm2.