Microstructure and Microhardness of High-Strength Aluminium Alloy Prepared Using High-Speed Laser Fabrication

Abstract

As a recently developed high-strength aluminium alloy used specifically for laser additive manufacturing, AlMgMnSc alloy possesses superior mechanical properties and excellent processability. Extreme high-speed laser deposition (EHLD) is a novel surface-modification technique, which is characterised by high depositing speed, rapid cooling, rate and minimal dilution rate. To offer a new method for surface repairing high-strength aluminium alloys, an AlMgMnSc alloy coating, containing two deposition layers, is prepared on a 6061 aluminium-alloy axle using the EHLD technique. Meanwhile, the microstructure, composition distribution, and microhardness variation of the fabricated coating are studied. The results reveal that the coating is dense and crack-free, which is well-bonded with the substrate. Additionally, layer 1 is mainly composed of large columnar and equiaxed grains, while layer 2 consists of a fully equiaxed grain structure with an average grain size of about 4.5 μm. Moreover, the microhardness of the coating (about 104~118 HV) is similar to the substrate (about 105 HV), proving the feasibility of repairing high-strength aluminium alloys using AlMgMnSc alloy powders through the EHLD technique.

Keywords

• microstructure
• microhardness
• composition
• grain structure
• high-strength aluminium alloy
• extreme high-speed laser deposition