Experimental Investigation into the Mechanical and Piezoresistive Sensing Properties of Recycled Carbon-Fiber-Reinforced Polymer Composites for Self-Sensing Applications

Abstract

This study investigates the mechanical and piezoresistive sensing properties of recycled carbon-fiber-reinforced polymer composites (rCFRPs) for self-sensing applications, which were prepared from recycled carbon fibers (rCFs) with fiber lengths of 6, 12, 18, and 24 mm using a vacuum infusion method. Mechanical properties of the rCFRPs were examined using uniaxial tensile tests, while sensing characteristics were examined by monitoring the in situ electrical resistance under cyclic and low fatigue loads. Longer fibers (24 mm) showed the superior tensile strength (92.6 MPa) and modulus (8.4 GPa), with improvements of 962.1% and 1061.1%, respectively. Shorter fibers (6 mm) demonstrated enhanced sensing capabilities with the highest sensitivity under low fatigue testing (1000 cycles at 10 MPa), showing an average maximum electrical resistance change rate of 0.7315% and a gauge factor of 4.5876. All the composites displayed a stable electrical response under cyclic and low fatigue loadings. These results provide insights into optimizing rCF incorporation, balancing structural integrity with self-sensing capabilities and contributing to the development of sustainable multifunctional materials.

Keywords

• recycled carbon fiber
• composite material
• mechanical properties
• sensing properties
• fiber-reinforced composite material