Developing high-strength ultrafine-grained pure Al via large-pass ECAP and post cryo-rolling

Abstract

In this paper, high-strength ultrafine-grained (UFG) pure aluminum (Al) was successfully achieved via a two-step processing route including room-temperature ECAP process for continuously 16 passes and post liquid nitrogen cryo-rolling for 50% reduction. The two-step processing route was observed to produce ultrafine grains with an average grain size of 0.98 μm and has obvious advantages for the preparation of high-strength pure Al in terms of the strength-ductility synergistic effect, which endows the pure Al excellent UTS value of 180 MPa, good Ef of 17.7% and a very high increase ratio (about 84%) of strength. The high strength was mainly attributed to the outstanding fine-grain strengthening provided by the combination of large-pass ECAP and cryo-rolling. In addition, the better uniform elongation of ECAP-rolled pure Al than ECAPed one was primarily dictated by the enhanced strain hardening capacity and the elongated grain shape.

Keywords

• Ultrafine-grained pure Al
• High strength
• Equal channel angular pressing
• Cryo-rolling