Effect of Preparation Method on the Catalytic Performance of HZSM-5 Zeolite Catalysts in the MTH Reaction

Abstract

A kind of nano-ZSM-5 zeolite crystal was synthesized by the hydrothermal method, and HZSM-5 zeolite powder was obtained via acid exchange. By using pseudoboehmite as a binder, a series of HZSM-5 zeolite catalysts for methanol-to-hydrocarbons (MTH) were prepared through adjusting the binder content between 20 and 50% in addition to the molding method of wet extrusion and mechanical mixing. XRD, 27Al NMR, SEM-EDS, ICP, low-temperature N2 adsorption and desorption, NH3-TPD, Py-FTIR, FT-IR, TG and elemental analyses were used to characterize the properties of fresh catalysts and coke-deposited catalysts. Then, MTH catalytic performance was evaluated in a continuous-flow fixed-bed reactor. The characterization and evaluation results showed that the addition of dilute nitric acid during the molding process increased the amount of moderate-strength acid and formed a hierarchical pore distribution, which helped to reduce the reaction ability of cracking, aromatization and hydrogen transfer, improve the diffusion properties of the catalyst and slow down the coke deposition rate. The catalyst with a binder content of 30% made by wet extrusion with dilute nitric acid had the best performance, whose activity stability of MTH increased by 96 h, higher than other catalysts, and the coke deposition rate was slower, which was due to the most suitable distribution of acid strength and B/L ratio as well as the most obvious hierarchical pore structure.

Keywords

• ZSM-5
• binder
• pseudoboehmite
• acid
• hydrocarbon
• coke