Synthesis of Zeolite A employing Amazon kaolin waste

Abstract

Abstract The synthesis of zeolite A employing kaolin waste from paper coating was studied. The kaolin waste was pre-treated at 550 to 800 ºC. For comparison purposes, a sample of zeolite A was also prepared using the IZA procedure. The materials were characterized by 27Al MAS NMR, X-ray diffraction and scanning electron microscopy using a microprobe. Pretreatment was necessary, and the best temperatures were between 600 and 700 ºC. The zeolite A formation was observed in all the prepared materials, reaching 52% crystallinity. On the other hand, the sodalite phase and amorphous materials were also formed.