Novel Bis(4-aminophenoxy) Benzene-Based Aramid Copolymers with Enhanced Solution Processability

Abstract

Aramid copolymers have garnered significant interest due to their potential applications in extreme environments such as the aerospace, defense, and automotive industries. Recent developments in aramid copolymers have moved beyond their traditional use in high-strength, high-temperature resistant fibers. There is now a demand for new polymers that can easily be processed into thin films for applications such as electrical insulation films and membranes, utilizing the inherent properties of aramid copolymers. In this work, we demonstrate two novel aramid copolymers that are capable of polymerizing in polar organic solvents with a high degree of polymerization, achieved by incorporating flexible bis(4-aminophenoxy) benzene moieties into the chain backbone. The synthesized MBAB-aramid and PBAB-aramid have enabled the fabrication of exceptionally thin, clear films, with an average molecular weight exceeding 150 kDa and a thickness ranging from 3 to 10 μm. The dynamic mechanical analysis (DMA) and thermogravimetric analysis (TGA) reveal that the thin films of MBAB-aramid and PBAB-aramid exhibited glass transition temperatures of 270.1 °C and 292.7 °C, respectively, and thermal decomposition temperatures of 449.6 °C and 465.5 °C, respectively. The mechanical tensile analysis of the 5 μm thick films confirmed that the tensile strengths, with elongation at break, are 107.1 MPa (50.7%) for MBAB-aramid and 113.5 MPa (58.4%) for PBAB-aramid, respectively. The thermal and mechanical properties consistently differ between the two polymers, which is attributed to variations in the linearity of the polymer structures and the resulting differences in the density of intermolecular hydrogen bonding and pi-pi interactions. The resulting high-strength, ultra-thin aramid materials offer numerous potential applications in thin films, membranes, and functional coatings across various industries.

Keywords

• aramid copolymer
• thin film
• extreme environment
• bar coating
• polymerization