A Study on the Microstructure and Mechanical Properties of Improved 25Ni-20Cr Steel via in Situ Testing

Abstract

To meet the application requirements for structural components in Gen-IV nuclear reactors, it is essential to improve the high-temperature mechanical properties of 25Ni-20Cr (S35140) austenitic stainless steel. In this research, an improved austenitic stainless steel (N-S35140), derived from S35140 steel, was investigated. The scanning transmission electron microscopy (STEM) results indicate that the addition of titanium (Ti) microalloying elements to S35140 steel led to the precipitation of new strengthening nano phases, including M(C, N), MC, MN and Ti(C, N), in N-S35140. These precipitates effectively compensated for the loss of high-temperature strength resulting from the substantial reduction in carbon content. During the in situ transmission electron microscopy (TEM) compressive process at room temperature, the yield strength of N-S35140 steel is 618.4 MPa. At room temperature, the tensile strength of N-S35140 steel is 638.5 MPa, with a yield strength of 392.8 MPa and an elongation of 32.7%, which surpasses those of S35140 steel at room temperature. N-S35140 steel exhibits a tensile strength of 330.6 MPa, a yield strength of 228.2 MPa, and an elongation of 51.4% during the in situ scanning electron microscopy (SEM) tensile test conducted at 650 °C. As a consequence, the improved N-S35140 steel demonstrates significantly enhanced mechanical properties compared to the original S35140 steel, positioning it as a promising candidate for structural components in Gen-IV nuclear reactors.

Keywords

• Gen-IV nuclear reactors
• N-S35140 austenitic steel
• mechanical properties
• TEM in situ compressive test
• SEM in situ tensile test