Influence of mechanical activation of a cordierite -based filler on sedimentation stability of lost foam refractory coatings

Abstract

For the development of the Lost Foam refractory coatings with controlled rheologic properties, the influence of the mechanical activation process on the cordierite-based filler’s properties change was examined. First of all, the test referred to the change of filler particles’ size and shape, as well as to dispersion ability and stability of the coating suspension. Cordierite was obtained by synthesis in a solid state, out of the mass consisting of kaoline, alumina, quartz, sepiolite. For characterization purposes, the following methods were used: X-ray diffraction, differential thermal analysis, SEM and optical microscopy. Mechanical activation of filler was performed in a vibrating mill. The upper boundary of the grain size was 100% -30 x 10-6 m, the times were (min): 15; 30; 60. The new composition of Lost foam refractory coatings has been developed with a change of the coating production process, as well. These newly synthesized coatings proved to be effective in terms of a positive influence on a surface quality, structural and mechanical properties of aluminium castings. Test results may be useful to have the Lost Foam refractory coatings specified together with other process parameters used for the production of castings according to this casting method. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. TR 33007, Grant no. 34006 and Grant no. 34013]

Keywords

• Cordierite
• Mechanical activation
• Lost Foam refractory coatings