Effect of bioceramic intracanal medication on the dentinal bond strength of bioceramic cements: an ex-vivo study

Abstract

Background The present study evaluated the effect of a bioceramic intracanal medicament (Bio-C Temp) on the push-out bond strength of bioceramic cements. Methods Forty-eight human single-canaled premolars were prepared and randomly divided into three groups: Group (A) received no intracanal medicament; Group (B) calcium hydroxide (CH); and Group (C) Bio-C Temp. After medicament removal, the roots were sectioned transversely. The slices in each group were separated into two subgroups (n = 16): in Subgroup (1), mineral trioxide aggregate (MTA) was placed, and in Subgroup (2) Bio-C Repair. Push-out bond strength was determined using a universal testing machine, applying a constant compressive force on the cement until bond failure. The failure mode was also evaluated. Data were analyzed using the Chi-square test and two-way ANOVA followed by Tukey’s post hoc tests. The level of significance was set at 5%. Results The pushout bond strength of Bio-C Repair was significantly higher than that of MTA irrespective of intracanal medication (p = 0.005). The placement of Bio-C Temp was associated with significantly lower bond strength (p = 0.002, p = 0.001). Conclusion Bio-C Repair showed better bond strength compared to MTA, irrespective of intracanal medication. Bio-C Temp intracanal medicament, however, decreased the bond strength of both these cements.

Keywords

• Bioceramic
• Calcium silicate
• Dentinal bond
• Intra canal medicament