Effects of the Volume Fraction of the Secondary Phase after Solution Annealing on Electrochemical Properties of Super Duplex Stainless Steel UNS S32750

Abstract

Super duplex stainless steel (SDSS) is used for manufacturing large valves and pipes in offshore plants because of its excellent strength and corrosion resistance. Large valves and pipes are manufactured by forging after casting, and the outside and inside microstructures are different owing to the difference in the cooling rate caused by the thermal conductivity. This microstructural variation causes cracks during solution annealing, which breaks the materials. To study the corrosion resistance of the SDSS forged material, the influence of the microstructure according to the difference between the inside and outside cooling rates of the cast SDSS was evaluated. To analyze the effects of the secondary phase fraction before solution annealing on the solution and corrosion resistance, the corrosion resistance with and without solution annealing was measured using the potentiodynamic polarization test and critical temperature test after the precipitation of the secondary phase. In the potentiodynamic polarization test, the secondary phase decreased the activation polarization and increased the corrosion rate. The critical pitting temperature exhibited the effect of the secondary phase.

Keywords

• corrosion properties
• super duplex stainless steel
• secondary phase
• solution annealing
• critical pitting temperature