Experimental Investigation of the Effect of Compressive Interface Stress on Interfaces in Reinforced Concrete Elements under Cyclic Action

Abstract

Reinforced concrete interfaces, either cracks within monolithic elements or joints between concretes cast at different times may become critical under cyclic actions, due to stiffness and interface resistance degradation. Among the numerous parameters affecting the behavior of interfaces, this paper focuses on the effect of externally applied compressive stress. In conjunction with this parameter, the diameter of the reinforcing bars crossing the interface, their embedment length, and the anchorage of the interface reinforcement, by bond or using epoxy resin, are investigated. Roughened concrete interfaces crossed by reinforcing bars were subjected to cyclic shear slips, with or without compressive stress normal to the interface. The presented experimental results prove the beneficial effect of the external compressive stress on the ultimate shear resistance of interfaces, accompanied by the reduction of the effect of small embedment length of the interface reinforcement, due to its reduced contribution: the externally imposed compression leads to smaller crack openings at the interface, in most cases smaller than 0.40 mm, and to reduction of the reinforcement clamping effect. The shear resistance is activated at reduced shear slip values (0.20 mm–0.40 mm compared to 0.20–0.80 mm for interfaces under zero external compression), while the interface resistance degradation is also reduced (e.g., during the second load cycle, to 15% on average, compared to 30% for interfaces under zero external compression). Finally, an equation previously proposed by the authors is applied for the prediction of the shear resistance of interfaces under normal force, leading to satisfying accuracy.

Keywords

• interface
• shear friction
• dowel action
• experimental investigation
• normal compressive stress