Development and Experimental Verification of Inorganic Electromagnetic Pulse Shielding Paint for Building Interiors Using Carbon-Based Materials

Abstract

The term electromagnetic pulse (EMP) generally refers to high-power electromagnetic waves and can be classified into EMPs caused by nuclear weapons, non-nuclear EMPs, and EMPs caused by natural phenomena. EMPs can cause catastrophic damage to any electronic device consisting of electromagnetic components, including communications devices and transportation. In this study, the shielding effectiveness of paint was evaluated depending on the type and content of carbon material and binder. To analyze the compatibility and dispersibility improvement of the raw materials used in paint manufacturing, experiments were conducted in two stages, using 27 mixtures. The shielding effectiveness was evaluated for the optimal mixture developed through mixture experiments. The results of this study confirmed that the developed EMP shielding paint can improve the shielding effectiveness of concrete by 25–40 dB. Additionally, the adhesion strength and moisture resistance evaluation of the EMP shielding paint were evaluated. The average adhesive strength of the EMP shielding paint was 1.26 MPa. In moisture-resistance testing at a temperature of 50 ± 3 °C and a relative humidity of 95% or higher for more than 120 h, no cracks or peeling were observed on the painted surface.

Keywords

• electromagnetic pulse
• shielding effectiveness
• inorganic
• paint
• carbon material