Effect of Cellulose Nanocrystals on the Coating of Chitosan Nanocomposite Film Using Plasma-Mediated Deposition of Amorphous Hydrogenated Carbon (a–C:H) Layers

Abstract

The substitution of petroleum-based polymers with naturally derived biopolymers may be a good alternative for the conservation of natural fossil resources and the alleviation of pollution and waste disposal problems. However, in order to be used in a wide range of applications, some biopolymers’ properties should be enhanced. In this study, biocompatible, non-toxic, and biodegradable chitosan (CS) film and CS reinforced with 10 wt% of cellulose nanocrystals (CN–CS) were coated with amorphous hydrogenated carbon layers (a–C:H) of different thickness. To investigate the effect of the nano-reinforcement on the a–C:H layer applied, mild radio frequency plasma enhanced chemical vapor deposition (RF-PECVD) was used to coat the CS and its CN–CS bio-nanocomposite film. Both the surface characteristics and the chemical composition were analyzed. The surface morphology and wettability were examined by ex-situ atomic force microscopy (AFM) and contact angle measurements (CA), respectively. Hereby, the relationship between sp2/sp3 ratios on a macroscopic scale was also evaluated. For the investigation of the chemical composition, the surface sensitive synchrotron X-ray radiation techniques near edge X-ray absorption fine structure (NEXAFS) and X-ray photoelectron spectroscopy (XPS) as well as diffuse reflectance infrared Fourier transform spectroscopy (DRIFT) were used.

Keywords

• cellulose microfibers
• bio-nanocomposite film
• radio frequency plasma enhanced chemical vapor deposition
• synchrotron-based analytics
• sp²/sp³ ratio
• substrate effects