The Influence of Process Parameters on the Surface Roughness of a 3D-Printed Co–Cr Dental Alloy Produced via Selective Laser Melting

Abstract

Selective laser melting (SLM), used to fabricate metallic objects with high geometrical complexity, is currently of increasing interest to the fields of medicine and dentistry. SLM-fabricated products should have highly smooth surfaces to minimize the use of post-processing procedures such as finishing and polishing. This study investigated the effect of various laser process parameters (laser power, scan rate, and scan-line spacing) on the surface roughness of a Co–Cr dental alloy that was three-dimensionally (3D) constructed via SLM. Initially, a single-line formation test was used to determine the optimal laser power (200 W) and scan rate (128.6 mm/s) that resulted in beads with an optimal profile. During subsequent multi-layer formation tests, the 3D Co–Cr body with the smoothest surface was produced using a scan-line spacing of 100 μm. The findings of this study show that laser process parameters have crucial effects on the surface quality of SLM-fabricated Co–Cr dental alloys.

Keywords

• Co–Cr alloy
• powder metallurgy
• selective laser melting
• surface roughness