In situ X-ray imaging of hot cracking and porosity during LPBF of Al-2139 with TiB2 additions and varied process parameters
Abstract
Laser powder bed fusion (LPBF) additive manufacturing of 2XXX series Al alloys could be used for low volume specialist aerospace components, however, such alloys exhibit hot cracking susceptibility that can lead to component failure. In this study, we show two approaches to suppress the formation of hot cracks by controlling solidification behaviour using: (1) TiB2 additions; and (2) optimisation of LPBF process parameters. Using high-speed synchrotron X-ray radiography, we monitored LPBF of Al-2139 in situ, with and without TiB2 under a range of process conditions. In situ X-ray radiography results captured the crack growth over 1.0 ms at a rate of ca. 110 mm s−1, as well as pore evolution, wetting behaviour and build height. High-resolution synchrotron X-ray computed tomography (sCT) was used to measure the volume fraction of defects, e.g. hydrogen pores and microcracks, in the as-built LPBF samples. Our results show adding TiB2 in Al-2139 reduces the volume of cracks by up to 79 % under a volume energy density of 1000 to 5000 J mm−3, as well as reducing the average length, breadth, and surface area of cracks.