Influences of Al concentration and Nb addition on oxidation behavior of Ti2AlC ceramics at high temperatures

Abstract

ABSTRACTA titanium aluminum carbide, Ti2AlC, which is classified among MAX phase ceramics, was studied as a potential candidate for various mechanical components used in high-temperature applications. The impact of its chemical composition on its high-temperature oxidation process was determined. Ti2AlC powders with various Al contents and with or without Nb addition were synthesized via a conventional reaction technique followed by 16 h of annealing in vacuum at 1300°C. The synthesized Ti2AlC powders were consolidated by means of 15 min of pulsed electric current sintering at a die temperature of 1300°C in vacuum under a uniaxial pressure of 30 MPa. In the presence of an aluminum reservoir in the form of TiAl3, Ti2AlC has excellent resistance against high-temperature oxidation. The promising results concerning the addition of Nb to TiAl provided the rationale for a similar modification of Ti2AlC. The results of oxidation tests on Nb-doped Ti2AlC likewise showed excellent oxidation resistance. Alloying with Nb can improve the oxidation resistance of Ti2AlC with low Al content, allowing the formation of a protective Al2O3 scale and inhibiting the growth of TiO2.

Keywords

• MAX phase
• Ti2AlC
• oxidation resistance
• Nb