Retrieval analysis of PEEK rods pedicle screw system: three cases analysis

Abstract

Abstract Purpose To analyze the characteristics of PEEK rods retrieved in vivo, specifically their wear and deformation, biodegradability, histocompatibility, and mechanical properties. Method Six PEEK rods were retrieved from revision surgeries along with periprosthetic tissue. The retrieved PEEK rods were evaluated for surface damage and internal changes using Micro-CT, while light and electron microscopy were utilized to determine any histological changes in periprosthetic tissues. Patient history was gathered from medical records. Two intact and retrieved PEEK rods were used for fatigue testing analysis by sinusoidal load to the spinal construct. Results All implants showed evidence of plastic deformation around the screw-rod interface, while the inner structure of PEEK rods appeared unchanged with no visible voids or cracks. Examining images captured through light and electron microscopy indicated that phagocytosis of macrophages around PEEK rods was less severe in comparison to the screw-rod interface. The results of an energy spectrum analysis suggested that the distribution of tissue elements around PEEK rods did not differ significantly from normal tissue. During fatigue testing, it was found that the retrieved PEEK rods cracked after 1.36 million tests, whereas the intact PEEK rods completed 5 million fatigue tests without any failure. Conclusion PEEK rods demonstrate satisfactory biocompatibility, corrosion resistance, chemical stability, and mechanical properties. Nevertheless, it is observed that the indentation at the junction between the nut and the rod exhibits relatively weak strength, making it susceptible to breakage. As a precautionary measure, it is recommended to secure the nut with a counter wrench, applying the preset torque to prevent overtightening.

Keywords

• PEEK rods
• Revision surgery
• Histological response
• Fatigue testing
• Retrieval analysis