Evaluación del comportamiento mecánico de compuestos PEI – fibra de vidrio ante solicitaciones térmicas
Abstract
The mechanical behavior of a composite with thermoplastic matrix and glass fiber reinforcement has been studied. It has been tested to constant stresses of a value equivalent to tensile strength divided by three to 50, 100 and 150 ºC, during periods of time between 250 and 3000 minutes. A decrement of the tensile strength and deformation can be observed in the three temperatures. Also a group of specimens have been exposed to accelerated aging in an environmental chamber to 70 ºC and 95% RH, during 30 days; and after they have been tested. In that case a decrement of the strength and deformation after 250 minutes has been observed, but in larger time of exposure these properties suffered an increment.<br><br>Se ha estudiado el comportamiento mecánico de un compuesto fabricado con un termoplástico PEI (polieterimida) reforzado con tejido de fibra de vidrio, frente a ensayos en los que se mantienen tensiones iguales a un tercio de su resistencia a tracción a 50, 100 y 150 ºC, durante periodos comprendidos entre 250 y 3000 minutos. En los resultados se observa una disminución de la resistencia y de la deformación en las tres temperaturas, con un mantenimiento de sus valores hasta las ensayadas a 3000 minutos. Además fueron expuestas un grupo de probetas del material, a envejecimiento acelerado en cámara higrotérmica a 70 ºC y a un 95% de H.R., durante 30 días; para luego someterlas a los ensayos antes descritos. Para esas probetas se obtuvieron pequeñas fluctuaciones de la resistencia y deformación con el tiempo, sin observarse una influencia significativa de la temperatura a la que se hicieron los ensayos termomecánicos.