Synthesis of Ultrahigh Molecular Weight Polymers with Low PDIs by Polymerizations of 1-Decene, 1-Dodecene, and 1-Tetradecene by Cp*TiMe₂(O-2,6-<i>ⁱ</i>Pr₂C₆H₃)–Borate Catalyst

Abstract

Polymerizations of 1-decene (DC), 1-dodecene (DD), and 1-tetradecene (TD) by Cp*TiMe2(O-2,6-iPr2C6H3) (1)−[Ph3C][B(C6F5)4] (borate) catalyst have been explored in the presence of Al cocatalyst. The polymerizations of DC and DD, in n-hexane containing a mixture of AliBu3 and Al(n-C8H17)3, proceeded with high catalytic activities in a quasi-living manner, affording high molecular weight polymers (activity 4120−5860 kg-poly(DC)/mol-Ti·h, Mn for poly(DC) = 7.04−7.82 × 105, after 20 min at −30 °C). The PDI (Mw/Mn) values in the resultant polymers decreased upon increasing the ratio of Al(n-C8H17)3/AliBu3 with decreasing the activities at −30 °C. The PDI values also became low when these polymerizations were conducted at low temperatures (−40 or −50 °C); high molecular weight poly(DD) with low PDI (Mn = 5.26 × 105, Mw/Mn = 1.16) was obtained at −50 °C. The TD polymerization using 1−borate−AliBu3 catalyst (conducted in n-hexane at −30 °C) afforded ultrahigh molecular weight poly(TD) (Mn = 1.02 × 106, Mw/Mn = 1.38), and the PDI values also decreased with increasing the Al(n-C8H17)3/AliBu3 ratio.

Keywords

• polymerization
• titanium complex
• catalyst
• α-olefin
• half-titanocene
• borate