Novel Micro-Mesoporous Composite ZSM-5 Catalyst for Aromatics Production by Catalytic Fast Pyrolysis of Lignin Residues

Abstract

The industrial utilization of lignocellulosic biomass is often accompanied by lots of lignin residues. Catalytic fast pyrolysis (CFP) is a high-throughput method to convert lignin to aromatics and phenolics. In order to optimize catalytic performance, conventional zeolite catalysts often need to have mesostructural modification. Here, based on hierarchical zeolite (HZ), a novel micro-mesoporous composite zeolite was obtained by redeposition under mild conditions. The conversion of two industrial lignin residues, Kraft Lignin (KL) and Pyrolytic Lignin (PL), was investigated. Interestingly, the hierarchical sample was more suitable for the case of higher concentration of primary pyrolysis products such as CFP of PL, with aromatics yield of 12.7 wt % and a monocyclic aromatic hydrocarbons (MAHs) to polycyclic aromatic hydrocarbons (PAHs) mass ratio of 4.86. The mesoporous composite zeolite possessed a better PAHs suppression capability as M/P reached 6.06, and was suitable for low reactants’ concentration and high oxygen content, such as KL CFP, with a higher aromatics yield of 3.3 wt % and M/P of 5.12. These results were compared with poplar sawdust as actual biomass, and mesoporous samples were both highly efficient catalysts with MAHs yield over 10 wt % and M/P around 5.

Keywords

• catalytic fast pyrolysis
• aromatics
• Kraft lignin
• pyrolytic lignin
• composite zeolite