Effects of 2% sodium fluoride solution on the prevention of streptococcal adhesion to titanium and zirconia surfaces

Abstract

Abstract Streptococci are associated with dental plaque formation as the early-colonizing bacteria that adhere to titanium (CpTi) and zirconia (TZP) implant abutment surfaces. Effective prevention of peri-implantitis may be possible by removing streptococci as target. This study aimed to evaluate the effects of 2% NaF on the prevention of streptococcal adhesion to CpTi and TZP. After immersion in 2% NaF for 90 min, surface characterization of mirror-polished CpTi and TZP disks were assesed using XPS, EPMA, and SEM. S. sanguinis, S. gordonii, and S. oralis were used as the streptococcal bacterial strains. After 24 h culture, bacterial adhesion was evaluated using an ATP-bioluminescent assay and SEM. In XPS, EPMA, and SEM analyses, fluoride was detected on the CpTi and TZP surfaces after 2% NaF immersion with no signs of localization, and no corrosion on the CpTi disks. Based on the adhesion assay, the adherences of S. sanguinis, S. gordonii, and S. oralis were significantly lower with NaF than without NaF in CpTi (p = 0.005, 0.001, and 0.001, respectively) and TZP (p = 0.003, 0.002, and 0.001). This was also confirmed by SEM. In conclusion, 2% NaF reduced the adhesion of streptococci to the CpTi and TZP surfaces.