Boletín de la Sociedad Española de Cerámica y Vidrio (Feb 2004)
Análisis microestructural por DRX de CaO obtenido a partir de carbonato cálcico molido (CCM)
Abstract
The development of limes obtained by firing of a ground calcium carbonate (GCC) from Clariana (Tarragona), at constant maximum temperature (960 ºC) and at different permanence times was studied. Reflections 111, 200, 220, 311, corresponding to structural planes of higher morphological appearance (and, as a result, of slower cristallite growing rate), are analized using a single line simplified XRD method. Values of cristallite size obtained by this way are significative different for the different studied directions, and range from 334 Å to 3796 Å. The order of cristallite growing rates is 1 1 1 < 1 0 0 < 1 1 0 < 3 1 1 which agrees the order of morphological prevalence, according to the Donay & Harker’s law.<br><br>Se estudia el desarrollo crstalino de CaO obtenido por calcinación (a temperatura máxima constante de 960ºC y distintos tiempos de permanencia) de un carbonato cálcico molido (CCM) proveniente de Clariana (Tarragona). Aplicando un método de análisis microestructural simplificado, de una sola línea, se analizan las reflexiones 111, 200, 220 y 311, asociadas a planos estructurales de mayor expresión morfológica y por ende de menor velocidad de crecimiento cristalino, obtienendose valores de tamaño de cristalito, con diferencias significativas para las distintas direcciones registradas y situados entre 334 y 3796 Å. El orden de las correspondientes velocidades de crecimiento de cristalito analizadas es 111 < 100 < 110 < 311, coincidente con el de preferencia morfológica establecida por la ley de Donay y Harker.