Anodic Dissolution Characteristics of GH4169 Alloy in NaNO₃ Solutions by Roll-Print Mask Electrochemical Machining Using the Linear Cathode

Abstract

GH4169 alloy/Inconel 718 is extensively utilized in aerospace manufacturing due to its excellent high temperature mechanical properties. Micro-structuring on the workpiece surface can enhance its properties further. Through-mask electrochemical micromachining (TMEMM) is a promising and potential processing method for nickel-based superalloys. It can effectively solve the problem that traditional processing methods are difficult to achieve large-scale, high-precision and efficiency processing of surface micro-structure. This study explores the feasibility of electrochemical machining (ECM) for GH4169 using roll-print mask electrochemical machining with a linear cathode. Electrochemical dissolution characteristics of GH4169 alloy were analyzed in various electrolyte solutions and concentrations. Key parameters including cathode sizes, applied voltage and corrosion time were studied in the roll-print mask electrochemical machining. A qualitative model for micro-pit formation on GH4169 was established. Optimal parameters were determined through experiments: 300 μm mask hole and cathode size, 10 wt% NaNO3 electrolyte, 12 V voltage, 6 s corrosion time. The results demonstrate that the micro-pits with a diameter of 402.3 μm, depth of 92.8 μm and etch factor (EF) of 1.81 show an excellent profile and localization.

Keywords

• GH4169 alloy
• through-mask electrochemical micromachining (TMEMM)
• process parameter optimization
• micro-pit structure forming