The effect of S/Mo ratio on structure and properties of MoSx-Ti composite coatings deposited by magnetron sputtering

Abstract

MoS _x -Ti composite coatings with different S/Mo ratios were prepared by varying the substrate bias voltage of magnetron sputtering. It was found that the S/Mo ratio of the as-deposited MoS _x -Ti coating decreased gradually from 1.7 to 1.3 as substrate bias voltage increased from −30 V to −110 V. The MoS _1.7 -Ti coating exhibits a nanocrystalline and amorphous phase mixed structure while the other MoS _x -Ti coatings were all amorphous structured. The hardness of the MoS _x -Ti coatings increased from 8.8 GPa to 9.8 GPa as the S/Mo ratio decreased from 1.7 to 1.3. The MoS _x -Ti coatings with the S/Mo above 1.4 exhibit COF with values smaller than 0.07 at RH of 50% and increased wear rate in the magnitude of ∼10 ^–7 mm ^3 Nm ^−1 . The tribological behavior of the MoS _x -Ti coatings were determined by the formation of the imperfect crystalline MoS _2 tribofilm. With the decrease of the S/Mo ratio, the increased defects in imperfect crystalline MoS _2 tribofilm lead to quicker consumption of the tribofilm during the trio-test, which result in a higher wear rate.

Keywords

• MoS2 coatings
• lubricious coatings
• tribological properties
• magnetron sputtering