A New Recycling Process for Tungsten Carbide Soft Scrap That Employs a Mechanochemical Reaction with Sodium Hydroxide

Abstract

WC soft scrap, including Co used as a binder, thermally oxidized at 600 °C, was subjected to grinding with NaOH in a mechanochemical reaction, followed by water leaching to establish an effective recycling process. Na2WO4 was synthesized through a mechanochemical (MC) reaction with oxidized scrap, and Na2CO3 was formed when the mixing ratio of NaOH increased. These as-synthesized compounds were water-soluble. When the weight ratio of soft scrap to NaOH was 1:0.5, 99.2% W was extracted by water leaching, while the extraction yield of Co was limited to 3.57% under the same conditions.

Keywords

• WC soft scrap
• thermal oxidation
• mechanochemical reaction
• sodium hydroxide
• water leaching