Spatial-Time Inhomogeneity Due to the Portevin-Le Chatelier Effect Depending on Stiffness

Abstract

This work is devoted to the study of the influence of the rigidity of the loading system on the kinetics of the initiation and propagation of the Portevin-Le Chatelier (PLC) strain bands due to the jerky flow in Al-Mg alloy. To estimate the influence of the loading system, the original loading attachment, which allows reducing the stiffness in a given range, was used. Registration of displacement and strain fields on the specimen surface was carried out with the Vic-3D non-contacting deformation measurement system based on the Digital Image Correlation (DIC) technique. The mechanical uniaxial tension tests were carried out using samples of Al-Mg alloy at the biaxial servo-hydraulic testing system Instron 8850. As a result of tensile tests, deformation diagrams were obtained for Al-Mg alloy samples tested at different values of stiffness of the loading system: 120 MN/m (nominal value), 50 MN/m, 18 MN/m, and 5 MN/m. All diagrams show discontinuous plastic deformations (the Portevin-Le Chatelier effect). It is noted that a decrease in the rigidity of the loading system leads to a change in the type of jerky flow. At constant parameters of the loading rate, temperature, and chemical composition of the material, the PLC effects of types A, B, and C are recorded in tests.

Keywords

• jerky flow
• Portevin-Le Chatelier effect
• strain band
• plasticity
• stiffness
• loading system