Effect of pre-strain on microstructure evolution and fracture behavior of undermatching X80 pipeline steel girth weld

Abstract

This work aims to study the effect of pre-strain on the fracture behavior of X80 pipeline girth weld joint, a comprehensive analysis was conducted on the microstructure and mechanical properties of the girth weld before and after pre-strain treatment. The mechanical properties were evaluated through tensile testing, Charpy impact testing, and digital image correlation (DIC) strain analysis. Furthermore, the microstructure and fracture morphology of the girth weld were observed using optical electron microscopy (OM) and scanning electron microscopy (SEM). The results show that the application of pre-strain treatment leads to dislocation accumulation at the grain boundary of X80 pipeline girth weld, resulting in stress concentration and subsequent formation of damage holes. This process disrupts the continuity of chain M-A island and initiates small cracks at the grain boundary, ultimately causing a significant decrease in impact toughness and impact work from 177 J to about 10 J.

Keywords

• pre-strain
• X80 pipeline steel
• girth-weld joint
• impact toughness