Ba0.5Sr0.5Co0.8Fe0.2O3–δ–La0.6Sr0.4Co0.8Fe0.2O3–δ Composite Cathode for Solid Oxide Fuel Cell

Abstract

Composite cathodes contain Ba0.5Sr0.5Co0.8Fe0.2O3–δ and La0.6Sr0.4Co0.8Fe0.2O3–δ were tested in different configuration for achieving cathode of area specific resistance lower than Ba0.5Sr0.5Co0.8Fe0.2O3–δ and La0.6Sr0.4Co0.8Fe0.2O3–δ cathodes. Electrodes were screen printed on samaria-doped ceria electrolyte half-discs and tested in the three electrode setup by the electrochemical impedance spectroscopy. Microstructure was observed by scanning electron microscopy. The lowest area specific resistance 0.46 and 2.77 Ω cm−2 at 700 °C and 600 °C respectively revealed composite cathode contain Ba0.5Sr0.5Co0.8Fe0.2O3–δ and La0.6Sr0.4Co0.8Fe0.2O3–δ in 1:1 weight ratio. The area specific resistance of this cathode is characterized by the lowest activation energy among tested cathodes.

Keywords

• barium strontium cobalt ferrite
• lanthanum strontium cobalt ferrite
• solid oxide fuel cell
• oxygen reduction reaction
• electrochemical impedance spectroscopy