Performance Comparison of Ferrite and Nanocrystalline Cores for Medium-Frequency Transformer of Dual Active Bridge DC-DC Converter

Abstract

This article reports an investigation into ferrite and nanocrystalline materials for the medium-frequency transformer of a dual active bridge DC-DC converter, which plays a key role in the converter’s efficiency and power density. E65 MnZn ferrite cores and toroidal and cut nanocrystalline cores are selected for the construction of 20-kHz transformers. Transformer performance is evaluated with a 1.1-kW (42–54 V)/400 V dual active bridge DC-DC converter with single-phase shift and extended phase shift modulations. The experimental results indicate that the toroidal nanocrystalline transformer had the best performance with an efficiency range of 98.5–99.2% and power density of 12 W/cm3, whereas the cut-core nanocrystalline transformer had an efficiency range of 98.4–99.1% with a power density of 9 W/cm3, and the ferrite transformer had an efficiency range of 97.6–98.8% with a power density of 6 W/cm3. A small mismatch in the circuit parameters is found to cause saturation in the nanocrystalline toroidal core, due to its high permeability. The analytical and experimental results suggest that cut nanocrystalline cores are suitable for the dual active bridge DC-DC converter transformers with switching frequencies up to 100 kHz.

Keywords

• dual active bridge DC-DC converters
• ferrite material
• nanocrystalline material
• soft magnetic material
• transformer