One-Step Synthesis of LiCo_1-1.5xY_xPO₄@C Cathode Material for High-Energy Lithium-ion Batteries

Abstract

Intrinsically low ion conductivity and unstable cathode electrolyte interface are two important factors affecting the performances of LiCoPO4 cathode material. Herein, a series of LiCo1-1.5xYxPO4@C (x = 0, 0.01, 0.02, 0.03) cathode material is synthesized by a one-step method. The influence of Y substitution amount is optimized and discussed. The structure and morphology of LiCo1-1.5xYxPO4@C cathode material does not lead to obvious changes with Y substitution. However, the Li/Co antisite defect is minimized and the ionic and electronic conductivities of LiCo1-1.5xYxPO4@C cathode material are enhanced by Y substitution. The LiCo0.97Y0.02PO4@C cathode delivers a discharge capacity of 148 mAh g−1 at 0.1 C and 96 mAh g−1 at 1 C, with a capacity retention of 75% after 80 cycles at 0.1 C. Its good electrochemical performances are attributed to the following factors. (1) The uniform 5 nm carbon layer stabilizes the interface and suppresses the side reactions with the electrolyte. (2) With Y substitution, the Li/Co antisite defect is decreased and the electronic and ionic conductivity are also improved. In conclusion, our work reveals the effects of aliovalent substitution and carbon coating in LiCo1-1.5xYxPO4@C electrodes to improve their electrochemical performances, and provides a method for the further development of high voltage cathode material for high-energy lithium-ion batteries.

Keywords

• lithium-ion battery
• high energy
• cathode
• LiCo_1-1.5xY_xPO₄@C