Efecto del BiFeO₃ en las propiedades del sistema ferroeléctrico libre de plomo K_0.5Na_0.5NbO₃

Abstract

In order to obtain a multiferroic material, powders and ceramic pieces, of the lead-free ferroelectric (1-x)-x K0.5Na0.5NbO3 (Bi0.8La0.2)FeO3 (KNN-BLFO) (x = 0.005, 0.010, 0.015, 0.020, 0.025) system were prepared using the combustion reaction method. For all the studied perovskite phase, stoichiometries feature KNN was obtained. Using characterisation techniques, it was determined that the BLFO is incorporated in the crystal structure of KNN without modifying present a phase transition. Moreover, It was also proved that the addition of the BLFO to KNN, alters the particle size of the obtained powders and generates magnetic behavior in this ferroelectric.En la búsqueda de un material multiferroico, se prepararon polvos y piezas cerámicas del sistema ferroeléctrico libre de plomo (1-x)K0.5Na0.5NbO3-x(Bi0.8La0.2)FeO3 (KNN-BLFO) (x=0.005, 0.010, 0.015, 0.020, 0.025), mediante el método de reacción por combustión. Para todas las estequiometrias estudiadas se obtuvo la fase perovskita característica del KNN. Con las diferentes caracterizaciones se determinó que el BLFO se incorpora en la estructura cristalina del KNN modificándola sin que se presente una transición de fase. Se comprobó además que la adición del BLFO al KNN, altera el tamaño de partícula de los polvos obtenidos y genera comportamiento magnético en este ferroeléctrico.

Keywords

• Multiferroic
• ferroelectric perovskite combustion
• Multiferroico
• ferroelectrico
• perovskita
• combustión