Enhancing the Mechanical Strength of a Photocurable 3D Printing Material Using Potassium Titanate Additives for Craniofacial Applications

Abstract

Photopolymerization-based three-dimensional (3D) printing techniques such as stereolithography (SLA) attract considerable attention owing to their superior resolution, low cost, and relatively high printing speed. However, the lack of studies on improving the mechanical properties of 3D materials highlights the importance of delving deeper into additive manufacturing research. These materials possess considerable potential in the medical field, particularly for applications such as anatomical models, medical devices, and implants. In this study, we investigated the enhancement of mechanical strength in 3D-printed photopolymers through the incorporation of potassium titanate powder (K2Ti8O17), with a particular focus on potential applications in medical devices. The mechanical strength of the photopolymer containing potassium titanate was analyzed by measuring its flexural strength, hardness, and tensile strength. Additionally, poly(ethylene glycol) (PEG) was used as a stabilizer to optimize the dispersion of potassium titanate in the photopolymer. The flexural strengths of the printed specimens were in the range of 15–39 MPa (Megapascals), while the measured surface hardness and tensile strength were in the range of 41–80 HDD (Hardness shore D) and 2.3–15 MPa, respectively. Furthermore, the output resolution was investigated by testing it with a line-patterned structure. The 3D-printing photopolymer without PEG stabilizers produced line patterns with a thickness of 0.3 mm, whereas the 3D-printed resin containing a PEG stabilizer produced line patterns with a thickness of 0.2 mm. These findings demonstrate that the composite materials not only exhibit improved mechanical performance but also allow for high-resolution printing. Furthermore, this composite material was successfully utilized to print implants for pre-surgical inspection. This process ensures the precision and quality of medical device production, emphasizing the material’s practical value in advanced medical applications.

Keywords

• 3D printing
• craniofacial application
• potassium titanate
• ceramic additive
• photocurable polymer