A New Approach for the Synthesis of Powder Zinc Oxide and Zinc Borates with Desired Properties

Abstract

Zinc borates are widely used in industry due to their thermal stability as a flame retardant in the production of plastics, rubber, and other polymer compositions. We have developed a simple and effective approach for the synthesis of zinc borate powders with desired properties, including desired particle size, low bulk density, high reactivity, etc. Zinc borates were prepared by the thermal treatment of a concentrated water–carbohydrate solution of a zinc salt until finely dispersed ZnO was formed, followed by its hydrothermal treatment at 90–300 °C as part of a suspension based on a hot aqueous solution of H3BO3. According to X-ray powder diffraction, IR spectroscopy, and TG–DSC data, depending on the temperature of hydrothermal treatment, a decrease in the water content in the structure of synthesized zinc borate particles is observed. TEM and SEM data indicate the formation of isometrically shaped zinc borate particles in the nanometer range during hydrothermal treatment above 250 °C. Varying the temperature of the hydrothermal treatment affects the average size and fineness of the structure of the zinc borate particles.

Keywords

• nanoscale zinc borate
• heat treatment
• concentrated water–carbohydrate salt solution
• hydrothermal treatment
• structure improvement
• structural water content