Nanomaterials (Sep 2019)

Short-Time Hydrothermal Synthesis of CuBi<sub>2</sub>O<sub>4</sub> Nanocolumn Arrays for Efficient Visible-Light Photocatalysis

  • Yi Wang,
  • Fang Cai,
  • Pengran Guo,
  • Yongqian Lei,
  • Qiaoyue Xi,
  • Fuxian Wang

DOI
https://doi.org/10.3390/nano9091257
Journal volume & issue
Vol. 9, no. 9
p. 1257

Abstract

Read online

In this article, a short-time hydrothermal method is developed to prepare CuBi2O4 nanocolumn arrays. By using Bi(NO3)3·5H2O in acetic acid and Cu(NO3)2·3H2O in ethanol as precursor solutions, tetragonal CuBi2O4 with good visible light absorption can be fabricated within 0.5 h at 120 °C. Tetragonal structured CuBi2O4 can be formed after 15 min hydrothermal treatment, however it possesses poor visible light absorption and low photocatalytic activity. Extending the hydrothermal treatment duration to 0.5 h results in a significant improvement invisible light absorption of the tetragonal CuBi2O4. The CuBi2O4 obtained through 0.5 h hydrothermal synthesis shows a band gap of 1.75 eV and exhibits the highest photocatalytic performance among the CuBi2O4 prepared with various hydrothermal time. The removal rate of methylene blue by the 0.5 h CuBi2O4 reaches 91% under visible light irradiation for 0.5 h. This study proposes a novel strategy to prepare photoactive CuBi2O4 nanocolumn arrays within 0.5 h at a moderate temperature of 120 °C. The hydrothermal method provides a facile strategy for the fast synthesis of metal-oxide-based photocatalysts at mild reaction conditions.

Keywords