The Effects of ZnO Additive on Sintering Behavior, Microstructural Evolution and Microwave Dielectric Properties of Li2TiO3 Ceramics

Abstract

The densification behavior, structural and microstructural evolution and microwave dielectric properties of Li2TiO3 + xZnO (x = 0, 0.5, 1, 1.5, 2, 3, and 5 mol%) ceramics have been investigated using X-ray diffraction, Field Emission Scanning Electron Microscopy, Raman spectroscopy and microwave resonant measurement. The Maximum density of 3.33 g/cm3 was obtained in Li2TiO3 + 2ZnO ceramic at low sintering temperature of 1100˚C. SEM investigations revealed good close packing of grains when x = 2 and preferential grain growth when x ≥ 3. The maximum values of Q × f = 31800 GHz and εr = 22.5 were obtained in Li2TiO3 + 3ZnO and Li2TiO3 + 2ZnO compositions, respectively. The observed properties are attributed to the microstructural evolution and grain growth (first case) or high density of the obtained ceramic (second case).

Keywords

• Li2TiO3
• ZnO addition
• Microwave dielectric properties
• Microstructure
• Sintering