Largely Enhanced Thermoelectric Power Factor of Flexible Cu_2−xS Film by Doping Mn

Abstract

Copper-sulfide-based materials have attracted noteworthy attention as thermoelectric materials due to rich elemental reserves, non-toxicity, low thermal conductivity, and adjustable electrical properties. However, research on the flexible thermoelectrics of copper sulfide has not yet been reported. In this work, we developed a facile method to prepare flexible Mn-doped Cu2−xS films on nylon membranes. First, nano to submicron powders with nominal compositions of Cu2−xMnyS (y = 0, 0.01, 0.03, 0.05, 0.07) were synthesized by a hydrothermal method. Then, the powders were vacuum-filtrated on nylon membranes and finally hot-pressed. Phase composition and microstructure analysis revealed that the films contained both Cu2S and Cu1.96S, and the size of the grains was ~20–300 nm. By Mn doping, there was an increase in carrier concentration and mobility, and ultimately, the electrical properties of Cu2−xS were improved. Eventually, the Cu2−xMn0.05S film showed a maximum power factor of 113.3 μW m−1 K−2 and good flexibility at room temperature. Moreover, an assembled four-leg flexible thermoelectric generator produced a maximum power of 249.48 nW (corresponding power density ~1.23 W m−2) at a temperature difference of 30.1 K, and had good potential for powering low-power-consumption wearable electronics.

Keywords

• Cu₂S
• thermoelectric
• hydrothermal synthesis
• doping
• flexible film